Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
12.5 g/10 min
Melt Volume Flow Rate (230 °C/2.16 kg)
14 cm³/10 min
Density (23 °C)
1.05 g/cm³
Flexural Modulus (23 °C, Tech. A)
2000 MPa
Tensile Modulus (23 °C)
1950 MPa
Tensile Stress at Yield (23 °C)
22 MPa
Tensile Strain at Yield (23 °C)
5 %
Charpy Impact Strength - Notched (23 °C)
8.5 kJ/m²
Charpy Impact Strength - Notched (0 °C)
4 kJ/m²
Charpy Impact Strength - Unnotched (23 °C)
100 kJ/m²
Charpy Impact Strength - Unnotched (0 °C)
50 kJ/m²
Vicat Softening Temperature (B50)
60 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed)
100 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed)
57 °C